Tribological performance of Nb-C thin films prepared by DC and HiPIMS

Autors/es

Sala, N.; Abad M.D.; Sánchez-López, J.C.; Cruz, M.; Caro, J.; Colominas, C.

Abstract

Nanostructured NbC thin films with variable contents of Nb and C were prepared by direct current (DC) magnetron sputtering, and for the first time, via high power impulse magnetron sputtering (HiPIMS) searching for an improvement in the tribological properties. X-ray diffraction shows that increasing the carbon incorporation, the crystalline composition evolves from Nb2C to NbC phase. Further carbon enrichment leads to a nanocomposite structure formed by small NbC crystals (8–14 nm) dispersed in a-C matrix. The friction coefficient varied from high friction (0.8) to low friction (0.25) and the hardness values between 20 and 11 GPa depending on the film composition. A densification of the coatings by changing the methodology from DC to HiPIMS was not observed.

WoS

Scopus

 

Altmetrics

  

 

Publicació

Material Letters, 15 October 2020, v.277, 128334

Data de publicació

2020-10-15

DOI

https://doi.org/10.1016/j.matlet.2020.128334